Pembuatan senyawa superkonduktor YBA2U3-X dengan bahan Y lokal

Purwito , Sostri (1995) Pembuatan senyawa superkonduktor YBA2U3-X dengan bahan Y lokal. Undergraduate thesis, FMIPA UNDIP.

[img]PDF
Restricted to Repository staff only

1655Kb
[img]
Preview
PDF
16Kb
[img]
Preview
PDF
336Kb
[img]
Preview
PDF
431Kb
[img]
Preview
PDF
372Kb
[img]
Preview
PDF
959Kb
[img]
Preview
PDF
444Kb
[img]PDF
Restricted to Repository staff only

465Kb
[img]
Preview
PDF
351Kb
[img]
Preview
PDF
346Kb

Abstract

ABSTRAK Senyawa superkonduktor YEla Cu 0 telah 2 3 7-x dibuat dari senyawa BaCOs • (99,9%), CuO (99,9%) lokal dengan kemurnian 90%, logam lain yang berhasil dan Y 0 2 terkandung adalah Gd dan Dy. Pengamatan gejala superkonduktivitas dari senyawa yang dihasilkaft didasarkan pada efek Meissner yaitu terangkatnya magnet cakram diatas sampel ketika dituangi dengan nitrogen cair sehingga meyakinkan bahwa senyawa yang dihasilkan adalah superkonduktor. Perilaku hambatan listrik terhadap temperatur sampel ditentukan dengan metode " probe " empat titik. Akan tetapi penurunan temperatur sampel hanya sampai pada 127 K. Sehingga diambil kesimpulan bah temperatur kritis T dari sampel berada dalam daerah temperatur kritis senyawa YBa Cu 0 dengan x = 0 yaitu 92 K sampai dengan titik 2 3 7-x didih dari nitrogen cair 77 K. ABSTRACT The YBa Cu 0 superconductor compound has been made 2: 3 7-x from BaCO3 (99,97.), CuO (99,97.) compound and Y 2 03 local with 907. purities and others metal consisted are Gd and Dy. The observation of superconductivity phenomenon from the result compound based on Meissner effect that is occurance flOating magnet disc over the sample when immersed with liquid nitrogen and it was proved that the compound is superconductor. The resistivity behavior at various sample temperature have been determined by four point probe method, but temperature decrease of the sample only to 1.27 K. So the conclusion is critical temperatOre of the sample lie within a range of critical temperature YBa Cu 0 compound with 2 3 7- x x = 0 that is 92 K to the boiling point of liquid nytrogen 77 K.

Item Type:Thesis (Undergraduate)
Subjects:Q Science > QC Physics
Divisions:Faculty of Science and Mathematics > Department of Physics
ID Code:30231
Deposited By:Mr UPT Perpus 1
Deposited On:24 Oct 2011 13:35
Last Modified:24 Oct 2011 13:35

Repository Staff Only: item control page