Pengaruh Lama Miling Terhadap Sifat Absorpsi Material Penyimpan Hidrogen MgH2 yang Dikatalisasi Dengan Fe (The Role of Milling Time on the Absorption Behaviour of MgH2 Catalyzed Fe)

Mustanir, M. and Zulkarnain, Jalil (2009) Pengaruh Lama Miling Terhadap Sifat Absorpsi Material Penyimpan Hidrogen MgH2 yang Dikatalisasi Dengan Fe (The Role of Milling Time on the Absorption Behaviour of MgH2 Catalyzed Fe). BULLETIN OF CHEMICAL REACTION ENGINEERING & CATALYSIS, 4 (2). pp. 69-72. ISSN 1978-2993

[img]
Preview
PDF - Published Version
490Kb

Official URL: http://bcrec.undip.ac.id/bcrec04022009p69-72

Abstract

Hidrida logam berbasis MgH2 dengan sisipan 1 wt% katalis Fe telah berhasil disintesis dengan teknik ball milling. Hasil proses miling selama 80 jam menunjukkan bahwa ukuran butir material telah membentuk struktur nanokristal. Hal ini ditunjukkan oleh profil difraksi sinar-X dimana terjadi pelebaran puncakpuncak difraksinya dengan meningkatnya waktu miling. Hasil uji absorpsi secara gravimetrik diketahui bahwa MgH2 berkatalis 1 wt% Fe mampu menyerap hydrogen sebesar 5,5 wt% dalam waktu ~20 menit pada temperatur 300 oC. Hasil ini sekaligus memperlihatkan bahwa sejumlah kecil katalis Fe bekerja secara baik dalam memperbaiki sifat absorpsi material penyimpan hydrogen berbasis Mg. (Metal hydrides are of great interest as hydrogen storage media especially for automotive application. Hydrides of magnesium and magnesium alloys are particularly attractive as they combine potentially high hydrogen storage capacities, 7.6 wt%. But, unfortunately, the sorption properties are poor. For example, conventional hydrogenation of magnesium requires prolonged treatment at temperatures of 300 oC and above. Here, we report the absorption properties of MgH2 catalyzed with a small amount of Fe element (1wt%) under argon atmosphere prepared by ball milling in 80 hours. As the results, it showed the influence of milling time on the absortion kinetics of material which could absorp hydrogen in amount 5.5 within 20 minutes at 300 oC. It is obvious that longer milling time and small amount of catalyst could improve the sorption properties of Mg-based hydrides).

Item Type:Article
Uncontrolled Keywords:Magnesium, ball milling, nanocrystalline, hydrogen absorption
Subjects:A General Works > AC Collections. Series. Collected works
T Technology > TP Chemical technology
Divisions:UNDIP Journal > Bulletin of Chemical Reaction Engineering and Catalysis
Faculty of Engineering > Department of Chemical Engineering
Faculty of Engineering > Department of Chemical Engineering
ID Code:7987
Deposited By:Dr. Istadi Istadi
Deposited On:31 Mar 2010 21:55
Last Modified:31 Mar 2010 21:55

Repository Staff Only: item control page