MODIFIKASI ALAT UJI BENDING SISTEM MEKANIK HIDROLIK DAN HASIL PENGUJIAN UNTUK BAHAN KUNINGAN ( MODIFICATIONS BENDING TEST EQUIPMENT HYDRAULIC MECHANICAL SYSTEMS AND MATERIALS TESTING RESULTS FOR BRASS )

Iskandar, Miftah Nova and Setyoko, Bambang (2016) MODIFIKASI ALAT UJI BENDING SISTEM MEKANIK HIDROLIK DAN HASIL PENGUJIAN UNTUK BAHAN KUNINGAN ( MODIFICATIONS BENDING TEST EQUIPMENT HYDRAULIC MECHANICAL SYSTEMS AND MATERIALS TESTING RESULTS FOR BRASS ). Undergraduate thesis, D3 Teknik Mesin Fakultas Teknik.

[img]
Preview
PDF
54Kb
[img]
Preview
PDF
26Kb
[img]
Preview
PDF
308Kb
[img]PDF
Restricted to Repository staff only

858Kb
[img]PDF
Restricted to Repository staff only

414Kb
[img]
Preview
PDF
21Kb

Abstract

Uji lengkung merupakan salah satu jenis pengujian bahan yang dilakukan untuk mengetahui sifat mekanik suatu bahan teknik. Di DIII Teknik Mesin memiliki alat uji bending dengan sistem dongkrak manual, dengan dongkrak manual maka daya yang dihasilkan dongkrak tergantung pada manusia yang menekannya. Modifikasi alat uji bending ini dilakukan untuk mengganti sistem kerja alat uji bending terdahulu yang menggunakan dongkrak manual menjadi sistem mekanik hidrolik dengan gear pump dan penggerak motor listrik. Pengujian terhadap bahan uji kuningan dengan tiga variasi dimensi yaitu 50x5x6 mm, 50x4x6 mm, 50x3x6 mm, dan metode yang digunakan dalam pengujian ini adalah three point bending dan four point bending. Data tekanan dongkrak, simpangan dan waktu penekanan diambil hingga spesimen/benda uji mendapatkan tekanan maksimal dari gaya tekan hidrolik. Hasil pengujian menunjukkan bahwa dimensi benda uji mempengaruhi gaya tekan yang terjadi pada saat pengujian. Semakin kecil dimensi yang di uji maka semakin kecil pula gaya tekan yang di timbulkan. Pada saat melakukan bending test, nilai rata-rata flexural strength yang didapatkan dengan menggunakan metode three point bending sebesar 275,75 kg/mm2 sedangkan untuk four point bending adalah 276,07 kg/mm2. Kata Kunci: Bending test, three point bending, four point bending, flexural strength, dimensi Bending Test is material testing to determine the mechanical properties of a material. Avaiable bending test equipment in Diploma III mechanical engineering faculty of engineering Universitas Diponegoro use hydrolic manual jack driving, the generated power depending on compressive force from the user. This Modified Bending Test change the previous Bending Test equipment working system use hydrolic manual jack driving to hydrolic mechanic system with gear pump and dynamo. Testing of yellow brass material with 4 different dimension is 50x5x6 mm, 50x4x6 mm,and 50x3x6 mm, using three point and four point bending method. Data of pressure jack, deviation, and pressure timing collect until the material obtain maximum pressure from hydrolic pressure.Testing results show the dimention of material affect the pressure value at the time of testing. The smaller the dimention of material test, the smaller pressure value obtained. While do the bending test, average flexural strength value collected from three point bending method is 275,75 kg/mm2. four point bending method is 276,07 kg/mm2 Keywords : Bending test, three point bending, four point bending, flexural strength, dimention

Item Type:Thesis (Undergraduate)
Subjects:T Technology > TJ Mechanical engineering and machinery
Divisions:Faculty of Engineering > Diploma in Mechanical Engineering
Faculty of Engineering > Diploma in Mechanical Engineering
ID Code:48236
Deposited By:Mrs Wahyu D3 Teknik Mesin
Deposited On:28 Mar 2016 07:55
Last Modified:28 Mar 2016 07:55

Repository Staff Only: item control page