Modifikasi zeolit alam ciptatujah untuk adsorben surfaktan anionik

Abstract

Zeolit alam dapat digunakan sebagai adsorben surfaktan anionik dengan odifikasi zeolit melalui proses dealuminasi, kalsinasi dan hidrotermal agar Si/Al, keasaman dan luas permukaan zeolit meningkat. Zeolit alam ujah direndam dalam HF 1% kemudian direfluk dengan HC1 6 N. jutnya proses kalsinasi dilakukan pada suhu 300 °C dan hidrotermal pada 350 °C menghasilkan zeolit-I. Zeolit-II dibuat dengan merendam zeolit HF 1 % kemudian direfluk dengan HCl 6 N dan diteruskan dengan ndam zeolit di dalam larutan NH4C1 0,1 N. Proses kalsinasi pada zeolit ini suhu 300 °C dan hidrotermal pada suhu 350 °C. Karakterisasi meliputi tuan rasio Si/Al, luas permukaan spesifik, total volume pori, keasaman dan than daya adsorpsi zeolit alam dan termodifikasi yaitu zeolit-I dan zeolit-II an menggunakan metode spektrofotometer serapan atom, BET, adsorpsi basa zeolit dan metode methylen blue active substance. Dari hasil memperlihatkan a rasio Si/Al zeolit bertambah dari 5,565 menjadi 6,282 untuk zeolit-I dan untuk zeolit-II. Keasaman zeolit dari 0,74 mmol/g menjadi 3,74 mmoVg zeolit-I dan 4,15 nunolig untuk Luas permukaan spesifik dan total e pori zeolit bertambah dari 72,101 m2Ig dan 47,621 10' mL/g menjadi 94 m2/g dan 84,367 le mL/g untuk zeolit-I, 127,487 m2/g dan 9 le mL/g untuk zeolit-IT. Adsorpsi Alkil Benzena Sulfonat (ABS) oleh t alam, zeolit-I dan zeolit-II adalah 38,05 %, 39,82 %, 45,13 % dan 10 mg/L Maka modiftkasi zeolit dengan dealuminasi beirganda dapat meningkatkan adsorpsi zeolit terhadap ABS. Natural zeolite can be used as anionic surfactan adsorbent by modification of t e zeolite to increase the Si/A1 rasio, acidity and surface area of zeolit by deal ination, calcination and hydrothermal processes. Natural zeolite of Cipa ujah was immersed in HF 1 % then in HCl 6 N. Sequently, calcination proc ss of zeolite at 300 °C and hydrothermal process at 350 °C produced zeoli e-I. Zeolite-11 was made by immersed zeolite in HF 1 % then in HC1 6 N and conti ued by immersed in NH4C1 0.1 N solution. Calcination process was cond cted at 300 °C and hydrothermal process at 350 °C. Characterize of the zeoli are the Si/Al rasio, spesific surface area, total pore volume, acidity and the perf• rmance of zeolit to Adsorpsie Alkil Benzene Sulfonat (ABS) so used Atoi is absorption spectrofotometer, Branauer, Emmet dan Teller (BET), bases adso ption by zeolite (NH3) and Methylen Blue Active Substance methods. The resul showed that the Si/Al ratio of zeolite increase from 5.565 to 6.282 for zeoli e-I and 7.724 for zeolite-II, zeolite acidity increase from 0.74 mmol/g to 3.74 mmol/g for zeolite-I and 4.15 mmol/g for zeolite-II. Specific surface area and ,otal pore volume of zeolite increase from 72.101 m2/g dan 47.621 10 mL/g to 156.294 m2/g and 84.367 10-3 inL/g for zeolite-I, 127.487 m2/g and 68.9°9 10-3 mL/g for zeolite-II. The adsorption of Alkil Benzene Sulfonat by natu al zeolite, zeolite-I and zeolite-II were 38.05 %, 39.82 % and 45.13 % from 10 g/L ABS, respectively. So modification of zeolite with twice dealumination coul a enhanched the adsorption of ABS.