Analisis faktor g pada bahan Paramagnetik DPPH yang terganggu Medan Listrik Statis

Susanti , Nunik Krisnawati (2001) Analisis faktor g pada bahan Paramagnetik DPPH yang terganggu Medan Listrik Statis. Undergraduate thesis, FMIPA UNDIP.

[img]PDF
Restricted to Repository staff only

1969Kb
[img]
Preview
PDF
17Kb
[img]
Preview
PDF
524Kb
[img]
Preview
PDF
434Kb
[img]
Preview
PDF
350Kb
[img]
Preview
PDF
621Kb
[img]
Preview
PDF
526Kb
[img]PDF
Restricted to Repository staff only

540Kb
[img]
Preview
PDF
337Kb
[img]
Preview
PDF
381Kb
[img]
Preview
PDF
617Kb

Abstract

Telah dilakukan pengukuran terhadap faktor "Lande" g pada bahan standar diphenyl-picryl-hidrazil (DPPH). Pengukuran faktor lande ini dilakukan pada dua kondisi bahan yakni bahan berada dalam pengaruh medan listrik dan tanpa pengaruh medan listrik. Penelitian dilakukan pada suhu kamar. Penelitian ini dilakukan dengan menggunakan metode ESR (Electron Spin Resonance) dengan memvariasi intensitas medan magnet B (0,13 mT — 1,83 inT) untuk memperoleh frekuensi resonansi spin elektron u (28,2 MHz — 75,5 MHz). Gangguan medan listrik (1,60 kV.cm-1 - 2,40 kV.cm-1) pada bahan dilakukan dengan menggunakan dua plat tembaga yang diberi beda tegangan DC (4kV, 5kV dan 6 kV). Nilai faktor "Londe" g yang diperoleh dari penelitian ini sebesar 1,9972 untuk tanpa gangguan; 2,0045 dengan gangguan sebesar 1,60 kV.cm-3; 2,0089 dengan gangguan sebesar 2,00 kV.cin-1; dan 2,0144 dengan gangguan sebesar 2,40 kV.ern-I. Peningkatan gangguan medan listrik akan memperbesar nilai faktor "Lande" g. The measurement of the Londe g-factor at standart substance diphenyl picryl-hydrazyl (DPPH) have been done at two condition which is substance consists of electrical fields influence and without electrical fields influence. The experiments have been done at the room temperature. This experiment was carried out by using Electron Spin Resonance ESR metode with variating intensity of the magnet fields B (0.13 mT-1.83 mT) to get the resonance frequency of spin electron (28.2 MHz-75.5 MHz). The perturbation of electric fields (1.60 kV.cm-1-2.40 kV .cm-l) in the substance using two copper plats with high DC .voltage.' The results of the values of the g-factor 1.9972 without perturbation; 2.0045 with perturbation in the amount of 1.60 kV.cm-1; 2.0089 with perturbation in the amount of 2.00 kV.cm-1; 2.0144 with perturbation in the amount of 2.40 kV.cm-t. The increation of electric fields perturbation will increase value of g-factor.

Item Type:Thesis (Undergraduate)
Subjects:Q Science > QC Physics
Divisions:Faculty of Science and Mathematics > Department of Physics
ID Code:30511
Deposited By:Mr UPT Perpus 1
Deposited On:01 Nov 2011 12:18
Last Modified:01 Nov 2011 12:18

Repository Staff Only: item control page