RANCANG BANGUN ALAT UJI BENDING SISTEM HIDROLIK DAN HASIL PENGUJIAN UNTUK BAHAN KUNINGAN ( BENDING DESIGN OF HYDRAULIC SYSTEM TEST EQUIPMENT AND MATERIALS TESTING RESULTS FOR BRASS )

Wijaya, Adhitya Chandra and Setyoko, Bambang (2011) RANCANG BANGUN ALAT UJI BENDING SISTEM HIDROLIK DAN HASIL PENGUJIAN UNTUK BAHAN KUNINGAN ( BENDING DESIGN OF HYDRAULIC SYSTEM TEST EQUIPMENT AND MATERIALS TESTING RESULTS FOR BRASS ). Undergraduate thesis, D3 Teknik Mesin.

[img]
Preview
PDF
199Kb

Abstract

Uji lengkung (bending test) merupakan salah satu jenis pengujian bahan yang dilakukan untuk mengetahui sifat mekanik suatu bahan teknik. Dalam prakteknya masih sedikit para praktisi pengujian bahan yang memperhatikan aspek dan pengaruh variasi dimensi benda uji terhadap data hasil uji lengkung. Untuk itu alat uji bending ini dibuat untuk mempelajari pengaruh variasi dimensi benda uji pada pengujian lengkung. Pengujian dilakukan dengan menggunakan alat uji bending sistem hidrolik dengan dimensi alat 600x75x750 mm. Dan pengujian terhadap bahan uji kuningan dengan tiga variasi dimensi yaitu 50x5x6 mm, 50x4x6 mm dan 40x3x6 mm, dan metode yang digunakan dalam pengujian ini adalah three point bending dan four point bending. Data tekanan dongkrak, simpangan dan waktu diambil hingga spesimen/benda uji mendapatkan tekanan maksimal dari gaya tekan hidrolik. Hasil pengujian menunjukkan bahwa dimensi benda uji mempengaruhi gaya tekan yang terjadi pada saat pengujian. Semakin kecil dimensi yang di uji maka semakin kecil pula gaya tekan yang di timbulkan. Pada saat melakukan bending test, nilai rata-rata flexural strength yang didapatkan dengan menggunakan metode trhee point bending sebesar 95.584 kg/mm2 dan pada saat melakukan pengujian dengan four point bending belum berhasil dikarenakan manometer yang digunakan tidak mencukupi kapasitasnya. Kata Kunci: Bending test, three point bending, four point bending, flexural strength, dimensi Bending test is one type of material testing conducted to determine the mechanical properties of a material engineering. In practice there are still few practitioners who pay attention to aspects of materials testing and the influence of variations in the dimensions of the specimen to bend test result data. For the bending test equipment is designed to study the effect of variations in the dimensions of the specimen on the test arch. Tests carried out using test equipment with a hydraulic system bending tool dimensions 600x75x750 mm. And testing of test material brass with three variations of dimensions 50x5x6 mm, mm 50x4x6 and 40x3x6 mm, and the methods used in this test is the three-point bending and four point bending. Jack pressure data, the deviation and the time taken until the specimen / test object to get the maximum pressure of the hydraulic pressstyle. Test results show that the dimensions of the specimen affects the compressive force that occurs during testing. The smaller dimensions in the smaller trials also compressive force that caused. At the time of bending test, the average value of flexural strength are obtained using methods trhee point bending at 95,584 kg/mm2 and during the four-point bending test has not been successful due to the manometer used is not sufficient capacity. Keywords: Bending test, three-point bending, four point bending, flexural strength, dimensional

Item Type:Thesis (Undergraduate)
Subjects:T Technology > TJ Mechanical engineering and machinery
Divisions:Faculty of Engineering > Diploma in Mechanical Engineering
Faculty of Engineering > Diploma in Mechanical Engineering
ID Code:29586
Deposited By:Mrs Wahyu D3 Teknik Mesin
Deposited On:05 Oct 2011 15:54
Last Modified:05 Oct 2011 15:54

Repository Staff Only: item control page