RANCANG BANGUN ALAT UJI BENDING SISTEM HIDROLIK DAN HASIL PENGUJIAN UNTUK BAHAN UJI KERAMIK ( DESIGN OF BENDING HYDRAULIC SYSTEM TEST EQUIPMENT AND MATERIALS TESTING RESULTS FOR CERAMIC TEST )

Yudha, Aditya Sandi and Setyoko, Bambang (2011) RANCANG BANGUN ALAT UJI BENDING SISTEM HIDROLIK DAN HASIL PENGUJIAN UNTUK BAHAN UJI KERAMIK ( DESIGN OF BENDING HYDRAULIC SYSTEM TEST EQUIPMENT AND MATERIALS TESTING RESULTS FOR CERAMIC TEST ). Undergraduate thesis, D3 Teknik Mesin.

[img]
Preview
PDF
154Kb

Abstract

Uji lengkung (bending test) merupakan salah satu jenis pengujian bahan yang dilakukan untuk mengetahui sifat mekanik suatu bahan teknik. Dalam prakteknya masih sedikit para praktisi pengujian bahan yang memperhatikan aspek dan pengaruh variasi dimensi benda uji terhadap data hasil uji lengkung. Untuk itu alat uji bending ini dibuat untuk mempelajari pengaruh variasi dimensi benda uji pada pengujian lengkung. Pengujian dilakukan dengan menggunakan alat uji bending sistem hidrolik dengan dimensi alat 600x75x750 mm. Dan pengujian terhadap bahan uji keramik dengan tiga variasi dimensi yaitu 50x40 mm, 50x30 mm dan 40x20 mm dengan merek yang berbeda-beda dan memiliki ketebalan berbeda pula yaitu 9 mm, 7 mm dan 6 mm sedangkan metode yang digunakan dalam pengujian ini adalah three point bending dan four point bending. Data tekanan dongkrak, simpangan dan waktu diambil hingga spesimen/benda uji mendapatkan tekanan maksimal dari gaya tekan hidrolik. Hasil pengujian menunjukkan bahwa dimensi benda uji mempengaruhi gaya tekan yang terjadi pada saat pengujian. Semakin kecil dimensi yang di uji maka semakin kecil pula gaya tekan yang di timbulkan. Pada saat melakukan bending test, nilai rata-rata flexural strength yang didapatkan dengan menggunakan metode three point bending untuk keramik tebal 9 mm sebesar 4,088 kg/mm2, tebal 7 mm sebesar 6,070 kg/mm2, tebal 6 mm sebesar 7,286 kg/mm2 dan pada saat melakukan pengujian dengan four point bending untuk keramik tebal 9 mm sebesar 1,146 kg/mm2, tebal 7 mm sebesar 1,562 kg/mm2, tebal 6 mm sebesar 3,507 kg/mm2 Kata Kunci: Bending test, three point bending, four point bending, flexural strength, dimensi Bend test (bending test) is one type of material testing conducted to determine the mechanical properties of a material engineering. In practice there are still few practitioners who pay attention to aspects of materials testing and the influence of variations in the dimensions of the specimen to bend test file result. For the bending test equipment is designed to study the effect of variations in the dimensions of the specimen on the test arch. Tests carried out using test equipment with a hydraulic system bending tool dimensions 600x75x750 mm. Trials and testing of ceramic materials with three-dimensional variations of 50x40 mm, 50x30 mm and 40x20 mm with different brands and have different thickness of 9 mm, 7 mm and 6 mm while the method used in this test is the three-point bending and four point bending. Jack pressure data, the deviation and the time taken until the specimen / test object to get the maximum pressure of the hydraulic press style. Test results show that the dimensions of the specimen affects the compressive force that occurs during testing. The smaller dimensions in the smaller trials also compressive force that caused. At the time of bending test, the average value of flexural strength are obtained using the method for the ceramics three point bending to 9 mm thickness of 4.088 kg/mm2, 7 mm thickness of 6.070 kg/mm2, 6 mm thickness of 7.286 kg/mm2 and the when tested with a four-point bending to 9 mm thickness of 1.146 kg/mm2, 7 mm thickness of 1.562 kg/mm2, 6 mm thickness of 3.507 kg/mm2. Keywords: Bending test, three-point bending, four point bending, flexural strength, dimensional

Item Type:Thesis (Undergraduate)
Subjects:T Technology > TJ Mechanical engineering and machinery
Divisions:Faculty of Engineering > Diploma in Mechanical Engineering
Faculty of Engineering > Diploma in Mechanical Engineering
ID Code:29585
Deposited By:Mrs Wahyu D3 Teknik Mesin
Deposited On:05 Oct 2011 15:30
Last Modified:05 Oct 2011 15:30

Repository Staff Only: item control page