PENGARUH VARIASI TEGANGAN LISTRIK DAN WAKTU PROSES ELEKTROPLATING TERHADAP KETEBALAN SERTA KEKERASAN LAPISAN PADA BAJA KARBON RENDAH DENGAN KROM

Raharjo, Samsudi (2010) PENGARUH VARIASI TEGANGAN LISTRIK DAN WAKTU PROSES ELEKTROPLATING TERHADAP KETEBALAN SERTA KEKERASAN LAPISAN PADA BAJA KARBON RENDAH DENGAN KROM. Masters thesis, UNIVERSITAS DIPONEGORO.

[img]
Preview
PDF - Published Version
12Mb

Abstract

ABSTRAK PENGARUH VARIASI TEGANGAN LISTRIK DAN WAKTU PROSES ELEKTROPLATING TERHADAP KETEBALAN SERTA KEKERASAN LAPISAN PADA BAJA KARBON RENDAH DENGAN KROM Samsudi Raharjo NIM L4E007017 Penggunaan baja pada masa sekarang ini sangatlah pesat, umumnya banyak digunakan untuk mengatasi alat-alat permesinan, konstruksi maupun pipa minyak atau gas. Peningkatan sifat-sifat fisis baja dapat dilakukan dengan proses pelapisan menggunakan metode electroplating. Tujuan penelitian ini adalah untuk membuktikan pengaruh variasi tegangan listrik dan waktu terhadap kekerasan serta ketebalan pada baja karbon rendah dengan pelapisan krom. Manfaat dilakukan penelitian yaitu untuk mendapatkan informasi pengaruh tegangan listrik dan waktu terhadap kekerasan serta ketebalan baja karbon rendah dengan pelapisan krom. Dalam kegiatan penelitian ini menggunakan baja karbon rendah yang dilapisi dengan menggunakan metode electroplating dengan variasi tegangan listrik 4, 6, 8, 10 dan 12 volt serta lama waktu pelapisan 5, 10, dan 15 menit. Selanjutnya dilakukan pengujian ketebalan serta kekerasan dan dianalisis dengan membangun persamaan matematik regresi polynomial orde tiga. Hasil penelitian ini menunjukan bahwa ketebalan lapisan krom keras pada tegangan 4, 6, 8, 10, 12 volt pada lama waktu, 15 menit: 7,76, 9,31, 17,85, 27,16, dan 37,79 µm kemudian nilai kekerasan menunjukkan 214,28, 232,92 , 254,77, 286,17, dan 351,29 VHN, lapisan pada struktur mikro merata dan baik serta hasil analisis regresi polynomial antara tegangan dan waktu terhadap ketebalan tegangan dan waktu terhadap kekerasan menunjukkan nilai determinat 0,999 dengan persamaan: Yt = 31,4 – 12,393 V + 1,8214 V2 – 0,0625 V3 dan Yh = 107,8 + 45,101V – 5,9464 V2 + 0,3229 V3. Kemudian dapat disimpulkan bahwa tebal lapisan krom keras serta kekerasan akan naik seiring dengan naiknya tegangan listrik dan waktu pada lama waktu proses elektroplating 15 menit. Kata kunci: volt, waktu, ketebalan, kekerasan, struktur mikro dan electroplating. iii ABSTRACT THE INFLUENCE OF ELECTRICAL VOLTAGE AND TIME VARIATIONS ON LAYER THICKNESS AND HARDNESS FOR ELECTROPLATING PROCESS OF LOW CARBON STEEL WITH CHROME Samsudi Raharjo NIM L4E007017 The usage of carbon steel at present is growing rapidly. The carbon steel is commonly used in the machining appliance and material construction, as well as oil or gas piping. Improvement of physical properties of steel can be performed by electroplating. The goal of this research was to prove the influence of electrical voltage and time variations on layer thickness as well as hardness of low carbon steel with chrome. The benefit of this research was to improve the physical and corrosion properties of steel for different application. In this research, low carbon steel was employed and platted by electroplating with variations of electrical voltage 4,6,8,10, 12 volt and times of 5, 10 and 15 minutes. Subsequently the thickness and hardness was determined and analyzed with the 3rd order polynomial regression. The result of this research showed that thickness of hard chrome at the voltage of 4, 6, 8 10, and 12 volt and the time of 15 minutes are 7,76, 9,31, 17,85, 27,16, and 37,79 µm. And the hardness values obtained are 214,28, 232,92, 254,77, 286,17, and 351,29 VHN. The layer of the material platted is quite uniform. The result of regression analysis for the voltage and time variations as function of the thickness provides determinant of 0,999 with equations of Yt = 31,4 – 12,393V + 1,8214V2 – 0,0625V3 and Yh = 107,8 + 45,101V – 5,9464V2 + 0,3229V3. It could be concluded that thickness and the hardness of chrome increase together with the increase of electrical voltage and time when the plating process is at 15 minutes. Key word: Electrical voltage, time, thickness, hardness, micro structure, low carbon steel and electroplating.

Item Type:Thesis (Masters)
Subjects:T Technology > TJ Mechanical engineering and machinery
Divisions:Postgraduate Program > Master Program in Civil Engineering
ID Code:23808
Deposited By:Mr UPT Perpus 2
Deposited On:08 Nov 2010 13:09
Last Modified:08 Nov 2010 13:09

Repository Staff Only: item control page